Productive & High Resolution
- 4K Resolution: 3840 X 2160 pixels
- Industrial grade superior UV optics & Light engine
- Largest printing platform among MiiCraft product lines (building size: 250x140x200mm)
Active peeling system
- Resin tank incorporates tilt motion to reduce peeling force during printing
- Enables efficient peeling of large areas and high viscosity resins
- Compatible with a wide range of resin types
Open material system and software
- Compatible with diversified materials.
- Supports integration with third-party CAD software
Specification
| Specification | Profession 250 | Profession 120 |
|---|---|---|
| Building size (mm) | 250 x 140 x 190mm | 120 x 67 x 190mm |
| Z-Layer Resolution | 12.5 μm to 500 μm | 12.5 μm to 500 μm |
| XY Resolution | 65 um | 30 um |
| Wavelength (LED) | 405/385nm | 405/385nm |
| I/O (Connection) | Ethernet / USB | Ethernet / USB |
| User Interface | 7” Touch Panel | 7” Touch Panel |
Applications
Jewelry
Manufacturing
Others
Jewelry
| No. | Model | Resin | Printing parameter | Post-procedure | Print-out examples | |
|---|---|---|---|---|---|---|
| Jewelry | ||||||
| 1 | Pro. 250 | BV-013A | Thickness : 50um Speed : slow Curing time : 8.5s Gap : 0 Base curing : 30s Base Layer : 1 Buffer layer :4 | Wash :Alcohol Post-Curing Energy : 30mw/cm2 Post-Curing time : 60min |  | |
| 2 | Pro. 250 | BV-013A | Thickness : 50um Speed : slow Curing time : 8.5s Gap : 0 Base curing : 30s Base Layer : 1 Buffer layer :4 | Wash :Alcohol Post-Curing Energy : 30mw/cm2 Post-Curing time : 60min |  | |
Manufacturing
| No. | Model | Resin | Printing parameter | Post-procedure | Print-out examples | |
|---|---|---|---|---|---|---|
| Manufacturing | ||||||
| 1 | Pro. 250Y | BV-022 | Thickness : 100um Speed : advanced Curing time : 1.8s Gap : 0 Base curing : 20s Base Layer : 1 Buffer layer :4 | Wash :Alcohol Post-Curing time : 10min |  | |
| 2 | Pro. 250Y | BASF | Thickness : 100um Speed : advanced Curing time : 5.5s Gap : 0 Base curing : 16s Base Layer : 1 Buffer layer :7 | Wash :Alcohol Post-Curing time : 3min |  | |
Others
| No. | Model | Resin | Printing parameter | Post-procedure | Print-out examples | |
|---|---|---|---|---|---|---|
| Others | ||||||
| 1 | Pro. 250 | BV-023A | Thickness : 100um Speed : advanced Curing time : 11.2s Gap : 0mm Base curing : 25s Base Layer : 6 Buffer layer : 6 | Wash : Alcohol Post-Curing Energy : 400mw/cm2 Post-Curing time : 15min |  | |
For more applications, please click on the icon below.